A new antibacterial coating made of poly(L-lysine)/hyaluronic acid (PLL/HA) multilayer films and liposome aggregates loaded with silver ions was designed. Liposomes filled with an AgNO 3 solution were first aggregated by the addition of PLL in solution. The obtained micrometer-sized aggregates were then deposited on a PLL/HA multilayer film, playing the role of a spacer with the support. Finally, HA/PLL/HA capping layers were deposited on top of the architecture to form a composite AgNO 3 coating. Release of encapsulated AgNO 3 from this composite coating was followed and triggered upon temperature increase over the transition temperature of vesicles, found to be equal to 34 degrees C. After determination of the minimal inhibitory concentration (MIC) of AgNO 3 in solution, the antibacterial activity of the AgNO 3 coating was investigated against Escherichia coli. A 4-log reduction in the number of viable E. coli cells was observed after contact for 120 min with a 120 ng/cm (2) AgNO 3 coating. In comparison, no bactericidal activity was found for PLL/HA films previously dipped in an AgNO 3 solution and for PLL/HA films with liposome aggregates containing no AgNO 3 solution. The strong bactericidal effect could be linked to the diffusion of silver ions out of the AgNO 3 coating, leading to an important bactericidal concentration close to the membrane of the bacteria. A simple method to prepare antibacterial coatings loaded with a high and controlled amount of AgNO 3 is therefore proposed. This procedure is far superior to that soaking AgNO 3 or Ag nanoparticles into a coating. In principle, other small bactericidal chemicals like antibiotics could be encapsulated by this method. This study opens a new route to modify surfaces with small solutes that are not permeating phospholipid membranes below the phase transition temperature.
Référence
Langmuir. 2008 Sep 16;24(18):10209-15