Comparison of the impact of preservation methods on amniotic membrane properties for tissue engineering applications.

Fiche publication

Date publication

novembre 2019

Journal

Materials science & engineering. C, Materials for biological applications

Auteurs

Membres identifiés du Cancéropôle Est :
Dr GINDRAUX Florelle

Tous les auteurs :
Fenelon M, Maurel DB, Siadous R, Gremare A, Delmond S, Durand M, Brun S, Catros S, Gindraux F, L'Heureux N, Fricain JC

Lien Pubmed

https://www.ncbi.nlm.nih.gov/pubmed/31500032

Résumé

Human amniotic membrane (hAM) is considered as an attractive biological scaffold for tissue engineering. For this application, hAM has been mainly processed using cryopreservation, lyophilization and/or decellularization. However, no study has formally compared the influence of these treatments on hAM properties. The aim of this study was to develop a new decellularization-preservation process of hAM, and to compare it with other conventional treatments (fresh, cryopreserved and lyophilized). The hAM was decellularized (D-hAM) using an enzymatic method followed by a detergent decellularization method, and was then lyophilized and gamma-sterilized. Decellularization was assessed using DNA staining and quantification. D-hAM was compared to fresh (F-hAM), cryopreserved (C-hAM) and lyophilized/gamma-sterilized (L-hAM) hAM. Their cytotoxicity on human bone marrow mesenchymal stem cells (hBMSCs) and their biocompatibility in a rat subcutaneous model were also evaluated. The protocol was effective as judged by the absence of nuclei staining and the residual DNA lower than 50 ng/mg. Histological staining showed a disruption of the D-hAM architecture, and its thickness was 84% lower than fresh hAM (p < 0.001). Despite this, the labeling of type IV and type V collagen, elastin and laminin were preserved on D-hAM. Maximal force before rupture of D-hAM was 92% higher than C-hAM and L-hAM (p < 0.01), and D-hAM was 37% more stretchable than F-hAM (p < 0.05). None of the four hAM were cytotoxic, and D-hAM was the most suitable scaffold for hBMSCs proliferation. Finally, D-hAM was well integrated in vivo. In conclusion, this new hAM decellularization process appears promising for tissue engineering applications.