Surface energy of hydroxyapatite and beta-tricalcium phosphate ceramics driving serum protein adsorption and osteoblast adhesion.
Fiche publication
Date publication
juin 2008
Auteurs
Membres identifiés du Cancéropôle Est :
Dr ANSELME Karine
Tous les auteurs :
dos Santos EA, Farina M, Soares GA, Anselme K
Lien Pubmed
Résumé
The main objective of this work was to evaluate the specific role of calcium phosphates surface energy on serum protein adsorption and human osteoblast adhesion, by isolating chemical effects from those caused by topography. Highly dense phosphate ceramics (single-phase hydroxyapatite HA and beta-tricalcium phosphates beta-TCP) presenting two distinct nano roughnesses were produced. Some samples were gold-sputter coated in order to conveniently mask the surface chemical effects (without modification of the original roughness) and to study the isolated effect of surface topography on cellular behavior. The results indicated that the nano topography of calcium phosphates strongly affected the protein adsorption process, being more important than surface chemistry. The seeding efficacy of osteoblasts was not affected nor by the topography neither by the calcium phosphate chemistries but the beta-TCP chemistry negatively influenced cell spreading. We observed that surface hydrophobicity is another way to change protein adsorption on surfaces. The decrease of the polar component of surface energy on gold-coated samples leaded to a decreased albumin and fibronectin adsorption but to an increased cell adhesion. Overall, this work contributes to better understand the role of topography and surface chemistry of calcium phosphates in serum protein adsorption and osteoblast adhesion.
Référence
J Mater Sci Mater Med. 2008 Jun;19(6):2307-16